Product DescriptionMV FRN616 is made using high-strength polyimide film and fluoropolymer materials. Combine polyimide and fluoropolymer materials to adapt to extreme environments. MV FRN616 film has
Order email
han.zhang09@china-venting.comMV FRN616 is made using high-strength polyimide film and fluoropolymer materials. Combine polyimide and fluoropolymer materials to adapt to extreme environments. MV FRN616 film has excellent electrical properties, heat resistance, chemical resistance properties and excellent bonding characteristics, and is suitable for aerospace wire and cable and high-performance electronic insulation fields.
ProductFeatures
Flame retardant UL94 V-0 grade
Meet the requirements of GJB 773B-2015and SAE AS22759
Applications
electronic insulation fields
Product specifications
| Product category | FEP（μm） | PI（μm） | FEP（μm） | Total thickness |
| （μm） | ||||
| MV FRN 015 | 0 | 25 | 12.5 | 37.5 |
| MV FRN 515 | 12.5 | 25 | 12.5 | 50 |
| MV FRN 025 | 0 | 50 | 12.5 | 62.5 |
| MV FRN 525 | 12.5 | 50 | 12.5 | 75 |
| MV FRN 616 | 2.5 | 25 | 2.5 | 30 |
| Number | Property | Unit | Test Method | MV FRN616 | MV FRT616 |
| Nominal | High tensile modulus | ||||
| 1 | Thickness | mm | ASTM D374 | 0.031 | 0.031 |
| 2 | Density | g/cm3 | ASTM D1004 | 1.7 | 1.75 |
| 3 | Tensile Strength | MPa | GB/T 1040 | 235 | 330 |
| 4 | Elongation | % | GB/T 1040 | 80 | 38 |
| 5 | Tensile Modulus | MPa | GB/T 1040 | 2357 | 6700 |
| 6 | Moisture Content | % | GB/T 1034 | ≤1.0 | ≤1.0 |
| 7 | Dielectric Strength | kV/mm | ASTM D149 | 180 | 180 |
| 8 | Volume Resistivity | Ω·cm | ASTM D257 | 2.31×1017 | 2.31×1017 |